Normac U-Repair 60NS Urethane Parts  "A" & "B"

Product Description:  A 100% solids plural component,  non-sag, urethane polymer system packaged in single and dual cartridges.

Material: MDI polyether and polyol.

Mix Ratio:    Part "A"    Part "B"
Weight:      100       92   

Volume:      1 part    1 part

Package Sizes:  Packaged/Sold by Volume

AVAILABILITY DETAILS

Sizes Part "A" Part "B"
Co-Axial 81g 76.5g
Universal 135g 137g
150x150 165g 153g
200x200 216g 204g
300x300 324g 306g
750x750 756g 714g

Normac U-Repair 60NS cartridges are packaged complete with 1 x static mixer and 1 x mixer locking nut in a nitrogen purged foil bag.

Application Life: 40 sec. @ 21oC (70oF)

Tack Free: 5 minutes @ 21oC (70oF)

Print Free: 10 minutes @ 21oC (70oF)

Hardness: 60 ± 5  Shore A

Bashore Resilience:  40% (ASTM D2632)

Impact Resistance: Greater than 160 inch - pounds (ASTM D2794)

Flexibility:  Pass 1/8" conical mandrel (ASTM D522)

Tear Strength: 66 pli D-470,  210 lbs. Die C

Tensile Strength: 950 psi (ASTM D412)

Elongation: 400% (ASTM D412)

Abrasion Resistance:  0.480 grams weight loss per 1000 cycles, H18wheel, at 1000 gms. (ASTM D1-044)

Operating Temp.:  -56oC (-70oF) to 93oC (200oF)

Fungus Resistance:  Non-nutrient

Weight of Cured Coating: 29 gm./m2 @ 25 microns  0.60 lbs. per 100 ft.2 at .001" thick

Modulus 100%:  385 psi (ASTM D412)

Ultimate Cure:  5 days at 30 dry mils at 21oC (70oF)

Recoat Times: 12 hours without surface preparation

Volatile Organic Compound (V.O.C.): Normac U-Repair 60NS is a 100% solids formulation and as a result has no VOCs.  It is advised to consider local, state, provincial or federal laws pertaining to the application of any coatings prior to use.

Mixed Solids Content: 100% by weight

Flash Point:  None, Normac U-Repair 60NS Part "A" and "B" are both non-flammable in shipping, storage and application.

Application:  Normac U-Repair 60NS is applied through low pressure single and dual cartridge dispensing equipment using 24 element static mixing tubes.

Surface Preparation: For best adhesion all surfaces should be properly prepared and the suitable primer/adhesive should be used. For more details see "Normac Surface Preparation Guide for Urethane Coatings" and Normac U-Repair Application data Sheets.

Primers:
NR-9500:  A two component, single coat air curing solvent based primer for bonding to metal, concrete, fiberglass and urethane.
900R:  A two component, air curing rubber based primer for bonding to rubber, PVC, urethane and foam.
NR-8400: A single component wash primer for bonding to rubber or urethane.
Refer to specific primer/adhesive data sheets.

Coverage:  Normac U-Repair 60NS:
Each 1 kg. of mixed product will theoretically yield:
34.0m2 @ 25 microns (367 ft2 @ .001"). See U-Repair Application Sheets.

   

NR-9500 PRIMER

Product Description

A 2-part polymeric resinous based adhesive for the bonding of the Normac series of sprayable urethanes, castables and trowelable putty syste...

Read more...

   

NR-8400 PRIMER

Product Description

A 1-part polymeric resinous based adhesive in Ethyl Acetate for bonding of the Normac U-Repair and BR-3TM series of elastomeric repair mater...

Read more...

   

Language  

   

Login  

   
© Normac Adhesive Products Inc.