NR-5SF SPRAYABLE URETHANE

Product Description
A solvent based urethane coating used in heavy abrasion situations designed primarily for application by airless spray. It can also be brushed, rolled or dipped.

Material: Aliphatic polyether urethane in dichloromethane.


Mix Ratio
NR-5SF Part A
NR-5SF Part B
By Weight 100 15

 

Package Sizes
  Packaged/Sold by Weight
Kit NR-5SF Part A
NR-5SF Part B
1.0kg 0.87kg 0.13kg
5.0kg 4.35kg 0.65kg
23kg 20.0kg 3.0kg
     
Solids Content
  Mixed  
By Weight   66.5%  

 

Hardness
Bashore Resilience
Tensile Strength
90±5 Shore A
40% (ASTM D2632-74) 4175psi (ASTM D412-68)

 

Impact Resistance
Flexibility
Tear Strength
Greater than 160 inch - pounds (ASTM D2794)
Pass 1/8" conical mandrel (ASTM D522) 450 lbs. Die C (ASTM D-624-73)

 

Elongation
Abrasion Resistance
Operating Temperature
320%
(ASTM D412-68)
0.0035 grams weight loss per 1000 cycles, H18 wheel, at 1000 gms. (ASTM D1-044-73) -56oC (-70oF) to 93oC (200oF)

 

Fungus Resistance
Modulus 100%
Weight of Cured Coating
Non-nutrient
1450 psi (ASTM D412-68)

43 gm/m2 @ 25 microns 0.90 lbs per 100 ft2 at .001" thick

 

Tack Free Print Free Ultimate Cure
1 hour @ 21oC (70oF) 3 hours @ 21oC (70oF) 5 days at 30 dry mils at 21oC (70oF)

 

Flammability
Normac NR-5S Part "A" and Part "B" are both non-flammable in shipping, storage and application. Flash Point: None

 

Recoat Times Application Life
Minimum: 10 - 15 minutes
Maximum: 72 hours.
1 hour plus, @ 21oC (70oF)

 

Volatile Organic Compound (V.O.C.)  
Methylene Chloride is not considered a V.O.C. Therefore the actual V.O.C. content will be less than 1%. It is advised to consider local, state, provincial or federal laws pertaining to the application solvent based coatings prior to use.  

Safety, Handling and Toxicity

See Normac NR-5SF MSDS documentation for specific handling and safe working practices.

 

Normac NR-5SF Part A MSDS

Normac NR-5SF Part B MSDS

 

Application
Normac NR-5SF can be sprayed, brushed, rolled or dipped. Spraying is the preferred method of application using standard air or airless spray equipment. Spray nozzle sizes depend upon the article being sprayed, usual range or nozzle openings would be from 0.015 inches to 0.035".

Surface Preparation: Standard surface preparation procedures such as grit blasting to near white/white metal or acid etching concrete is required for good mechanical bonding of the Normac NR-5SF sprayable urethane system. For more details see "Normac Surface Preparation Guide for Urethane Coatings."

Primers:
NR-8310: A single component, moisture cure primer.
NR-9500: A two component, single coat air curing solvent based primer.
NR-9600: A two component wash primer base for NR-9500.
900R/ECR: A two component, air curing rubber based primer.
EP-100: A two component 100% solids primer for concrete.

 

Coverage
22.7m2 @ 25 microns/kg DFT (111 ft2/lb@ .001" DFT). 0.57m2 @ 1mm DFT thickness per kg. (6.11ft2/.040"/lb.DFT).


Rev.4

   

NR-9500 PRIMER

Product Description

A 2-part polymeric resinous based adhesive for the bonding of the Normac series of sprayable urethanes, castables and trowelable putty syste...

Read more...

   

NR-T10 ADDITIVE

Product Description

NR-T10 is a thixotropic agent that when added to our solvent based sprayable urethanes, allows the applicator to apply wet film coating thi...

Read more...

   

NR-9600 PRIMER

Product Description

A 2-part polymeric resinous based wash primer used in conjunction with Normac’s NR-9500 2 part primer system for the bonding of the Normac...

Read more...

   

NR-8400 PRIMER

Product Description

A 1-part polymeric resinous based adhesive in Ethyl Acetate for bonding of the Normac U-Repair and BR-3TM series of elastomeric repair mater...

Read more...

   

Product Menu  

   

Language  

   

Login  

   
© Normac Adhesive Products Inc.