Product Description
A solvent based urethane coating used in heavy abrasion situations designed primarily for application by airless spray.  It can also be brushed, rolled or dipped.

Material: Aliphatic polyether urethane in dichloromethane.

Mix Ratio
NR-5S Part A
NR-5S Part B
By Weight 100 20


Package Sizes
  Packaged/Sold by Weight
Kit NR-5S Part A
NR-5S Part B
1.0kg 833g 167g
4.8kg 4kg 8kg
24kg 20.0kg 4.0kg
Solids Content
By Weight    66.5%  


Bashore Resilience
Tensile Strength
90┬▒5 Shore A
40% (ASTM D2632-74) 4175psi (ASTM D412-68)


Impact Resistance
Tear Strength
Greater than 160 inch - pounds (ASTM D2794)
Pass 1/8" conical mandrel (ASTM D522) 450 lbs. Die C (ASTM D-624-73)


Abrasion Resistance
Operating Temperature
(ASTM D412-68)
0.0035 grams weight loss per 1000 cycles, H18 wheel, at 1000 gms. (ASTM D1-044-73) -56oC (-70oF) to 93oC (200oF)


Fungus Resistance
Modulus 100%
Weight of Cured Coating
1450 psi (ASTM D412-68)

43 gm/m2 @ 25 microns 0.90 lbs per 100 ft2 at .001" thick


Tack Free Print Free Ultimate Cure
1 hour @ 21oC (70oF) 3 hours @ 21oC (70oF) 5 days at 30 dry mils at 21oC (70oF)


Normac NR-5S Part "A" and Part "B" are both non-flammable in shipping, storage and application. Flash Point: None


Recoat Times Application Life
Minimum: 10 - 15 minutes
Maximum: 72 hours.
1 hour plus, @ 21oC (70oF)


Volatile Organic Compound (V.O.C.)  
Methylene Chloride is not considered a V.O.C. Therefore the actual V.O.C. content will be less than 1%. It is advised to consider local, state, provincial or federal laws pertaining to the application solvent based coatings prior to use.  

Safety, Handling and Toxicity

See Normac NR-5S MSDS documentation for specific handling and safe working practices.


Normac NR-5S Part A MSDS

Normac NR-5S Part B MSDS




Normac NR-5S can be sprayed, brushed, rolled or dipped. Spraying is the preferred method of application using standard air or airless spray equipment. Spray nozzle sizes depend upon the article being sprayed, usual range or nozzle openings would be from 0.015 inches to 0.035".

Surface Preparation: Standard surface preparation procedures such as grit blasting to near white/white metal or acid etching concrete is required for good mechanical bonding of the Normac NR-5S sprayable urethane system. For more details see "Normac Surface Preparation Guide for Urethane Coatings."

NR-8310: A single component, moisture cure primer.
NR-9500: A two component, single coat air curing solvent based primer.
NR-9600: A two component wash primer base for NR-9500.
900R/ECR: A two component, air curing rubber based primer.
EP-100: A two component 100% solids primer for concrete.


22.7m2 @ 25 microns/kg DFT (111 ft2/lb@ .001" DFT). 0.57m2 @ 1mm DFT thickness per kg. (6.11ft2/.040"/lb.DFT).