Normac NR-6511D Parts "A" and  "B"

Product Description: A 100% solids Heated Plural Component High Performance Modified Polyurea Spray System designed for superior chemical and heat resistant applications such as tank linings, ponds, reservoirs and concrete containment areas.

Material: Polyurea Hybrid

Mix Ratio:                         Part "A"       Part "B"

By Weight:                            100               90       

By Volume:                           100             100

Package Sizes:  Packaged/Sold by Weight

Kit                                     Part "A"       Part "B"

  38 kg. (A+B)                     20.0 kg.     18.0 kg.

431.82 kg. (A+B)                227.27 kg.    204.55 kg.

Viscosity @ 21oC(70oF)      Part AA@     Part AB@

                  500cps          550cps

Pot Life:                 6 to 10 seconds

Tack Free:              less than 25 seconds

Hardness:               60 + 5  Shore D

Impact Resistance:

Greater than 160 inch - pounds (ASTM D-2794)

Tear Strength:       415 pli Die AC@

                              107 pli ASTM D-470

Tensile Strength:  2350 psi (ASTM D-412)

Elongation:           175% (ASTM D-638)

Abrasion Resistance:  0.200 grams weight loss per 1000 cycles, H22 wheel, at 1000 gms. (ASTM D1-044)

Operating Temperature:  -56oC (-70oF) to 93oC (200oF)

Fungus Resistance:          Non-nutrient

Elcometer Adhesion:

                    Steel:     >1500 psi (ASTM D-4541)

              Concrete:     > 900 psi (ASTM D-4541)

Vapor Transmission:   < 0.10 (ASTM E96-80)

Weight of Cured Coating: 29 gm./m2 @ 25 microns 0.60 lbs. per 100 ft.2 at .001" thick

Ultimate Cure:  5 days at 21oC (70oF)

Recoat Times:  Continuous: Maximum 12 hours

Mixed Solids Content: 100%

Flash Point:  None, Normac NR-6511D Part "A" and "B" are both non-flammable in shipping, storage and application. See Material Safety Data Sheet (MSDS).

Application:   Normac NR-6511D is applied through heated plural component 1:1 equipment.  The recommended spray gun is a Probler or Gusmer GX-7 with the appropriate mixing nozzle or chamber. This system uses air pressure to purge the mix chambers and tips.  No solvent is required during application.  Typical operating temperatures are between 60oC (140oF) to 71oC (160oF). Spraying pressures should be minimum 2500psi for best physicals.  Air requirements for the main pumps is 90 lbs. Electrical is 220v single phase and 110v.

Surface Preparations and Primers:  Standard surface preparation procedures such as grit blasting to near white metal or acid etching concrete is required for good mechanical bonding of the NR-6511D sprayable polyurea system. See "Normac Surface Preparation Guide for Urethane Coatings".

Primers:

NR-9500:  A two component, single coat air curing solvent based primer.

EP100/EP200:  A two component, air curing epoxy based primer.

Refer to specific primer/adhesive data sheets.

Coverage: Normac NR-6511D

Theoretical coverage:

34 m2 @ 25 microns (166 ft2/lb. at .001").


Rev.2
   